Proceeding Abstracts
-
Objective:
Retention and resistance of the implant-tissue supported overdenture may be affected by the type of attachment. The aim of this research was to compare the retention and resistance of Nobel Biocare Ball (NBB), Nobel Biocare Bar and Clip (NBBC) and Sterngold ERA Red (ERAR) attachments on an implant-tissue supported overdenture model.
Materials and Methods:
The attachment samples were divided into 3 groups of NBB, NBBC, and ERAR (5 samples in each group). Two parallel Nobel Biocare Branemark implants were placed symmetrically at the symphysis region of a mandibular test model. A metallic overdenture was fabricated precisely adapted to the model and attached to a Zwick testing machine (crosshead speed of 51 mm/min). Dislodging tensile forces were applied in three vertical, oblique, anterior-posterior directions and two situations, at the beginning and after 100 times of insertion/removal of the overdenture, for each sample. The maximum dislodging force was measured. A One-way ANOVA test was employed followed by Tukey's test.Results:
ERAR was the most retentive and resistant in both situations. NBB and NBBC showed the same anterior-posterior resistance at the beginning. All test groups represented a large amount of retention and resistance loss after the insertion/removal of the overdenture, while NBBC showed a higher loss of anterior-posterior resistance than NB.Conclusion:
A highest level of retention and resistance was seen in ERAR. The retention and resistance were affected by the wear of attachments. -
Introduction:
Melanin pigmentation in the oral mucosa occurs as a result of several reasons one of which is smoking. Cigarette smoke induces numerous side effects in the people who do not smoke, but are in the same environment. The aim of this study was to evaluate the role of parental smoking on pigmentation of their children's oral mucosa.
Materials and Methods:
This study was carried out as a historical cohort. Participants were 400 healthy children, 10 to 11 years old who did not use any drugs. The passive smoker group included 200 children who at least one member in their family was a smoker. The control group included 200 children who did not have a smoker in their family. Furthermore, two groups were matched in the point of view of skin color. The children in the two groups were examined and oral pigmentation was recorded. Finally, the results were analyzed by the chi- square test.
Results:
Pigmentation was seen in 150 children (75%) in the experimental group and 122 children (61%) in the control group (P<0.005). The relative risk of oral pigmentation for children who were exposed to passive smoking was 1.23.
Conclusion:
Based on the results of this study, passive smoking can induce gingival pigmentation in children.
-
Objective:
Contradictory results have been reported over microleakage studies of restorative materials and methods. Despite the number of publications on leakage there are few evidences comparing the different microleakage evaluation methods. The purpose of the present study was to compare the clearing technique and longitudinal sectioning in the evaluation of dye penetration along a glass fiber post.
Materials and Methods:
Fifteen single-rooted human teeth were endontically prepared and obturated with gutta percha points and a resin based sealer (AH26). A glass fiber post (Glassix) was cemented into each post space with a dual polymerizing resin cement (Varilink II) and the composite core (Tetric Ceram) was fabricated. Specimens were immersed in Indian ink solution for 72 hours after completion of 1500 cycles of thermal cycling. Then demineralized, cleared and evaluated for the deepest length of dye penetration using a stereomicroscope. Specimens were then cut longitudinally and the length of penetration was measured again by the same instrument. The mean difference of the penetrated length was analyzed by two methods using the paired t test and an analysis of correlation ( = 0.05).Results:
No significant difference was found in the mean microleakage measured by the twomethods (P= 0.07). Significant correlation was found between them (P=0.0001, r= 0.9)Conclusion:
The clearing technique and longitudinal sectioning showed the same results in microleakage of Glassix post and composite core within the limitation of the present study. -
Objective:
This study evaluated the effect of saliva contamination during bonding procedures without removing saliva on shear dentin bond strength of three adhesive generations when rubber dam isolation is not feasible.
Materials and Methods:
Flat superficial dentin surfaces of seventy-two extracted human molars were randomly divided into three groups (A: Scotch Bond MP Plus (SBMP), B: Single Bond (SB), C: Prompt L-Pop) according to the applied adhesives and twelve subgroups (n=6) according to the following saliva contamination applied in different bonding steps. The specimens were contaminated with saliva after etching (A1 and B1), after primer application (A2), after adhesive application before polymerization (A3, B2 and C1), and after adhesive polymerization (A4, B3 and C2). Three subgroups were not contaminated as controls (A5, B4 and C3). Resin composite was placed on dentin subsequently followed by thermocycling. Shear test was performed by Universal testing machine at 0.5 mm/min crosshead speed. The collected data were statically analyzed using one and two-way ANOVA and Tukey HSD.Results:
In contrast to SBMP and SB, the mean shear bond strength of Promote L-Pop was not significantly different between contaminated and uncontaminated subgroups. Mean shear bond strengths of SBMP subgroups contaminated after adhesive polymerization or uncontaminated were significantly higher compared to the other two groups (p<0.05).Conclusion:
Unlike Promote L-Pop, saliva contamination could reduce shear bond strength of the total-etch adhesives. Furthermore, the step of bonding procedures and the type of adhesive seems to be effective on the bond strength of adhesive contaminated with saliva. -
Introduction:
Whitening toothpastes which have been accepted in populations may affect properties of enamel and restorative materials. The aim of this study was to compare the microhardness of human enamel and Z250 microhybrid composite resin after brushing with two whitening toothpastes.
Materials and Methods:
In this experimental study of enamel specimens, forty five freshly extracted human incisors were prepared and divided into three groups of control enamel (ClE), Crest enamel (CtE) and Aquafresh enamel (AfE). For composite resin specimens, forty five cylindrical-shaped specimens of light-cured Z250 composite were prepared and divided into three groups of control composite (ClC), Crest composite (CtC) and Aquafresh composite (AfC). The control groups were brushed without toothpaste. Crest and Aquafresh group specimens were brushed with Crest and Aquafresh whitening toothpastes, respectively. Vickers microhardness test wasperformed for all groups. Data were analyzed by One-way ANOVA and Tukey tests.Results:
Microhardness values of ClE, CtE, AfE, ClC, CtC and AfC groups were332.99 ± 26.59, 313.99 ± 20.56, 323.57 ± 27.96, 137.1 ± 3.16, 122.95 ± 3.27 and 130.36 ± 4.8, respectively. One-way ANOVA showed no significant differences among three enamel groups but there was significant difference among composite groups (p<0.01).Conclusion:
Crest and Aquafresh whitening toothpastes did not affect enamel hardness but reduced the microhardness value of Z-250 composite resin. However, Crest whitening toothpaste decreased the microhardness more than Aquafresh. -
Introduction:
In cases of severe hard tissue loss, 2 mm circumferential ferrule is difficult to achieve. So in these cases we should use different ferrule designs. This in vitro study investigated the effect of different ferrule designs on the fracture resistance of teeth restored with bonded post and cores.
Materials and Methods:
Forty freshly-extracted central incisors were endodontically treated. The teeth were randomly divided into four groups; group 1 were teeth with 2 mm circumferential ferrule above the CEJ, group 2 were teeth with 2 mm ferrule only on the palatal side of the teeth, group 3 consisted of teeth with 2 mm ferrule only on the facial side and group 4 were teeth with 2 mm ferrule on the palatal and facial side of teeth with interproximal concavities. All teeth were restored with fiber posts and composite cores. The specimen was mounted on a universal testing machine and compressive load was applied to the long axis of the specimen until failure occurred.Results:
The fracture resistance was 533.79 ± 232.28 in group 1, 634.75± 133.35 in group 2, 828.90 ±118.27 in group 3 and 678.78± 160.20 in group 4. The post hoc analysis showed statistically significant difference between groups 1 and 3 .Conclusions:
The results of this in vitro study showed that facial ferrule increases the fracture resistance of endodontically treated teeth restored with bonded post and cores. -
Objective:
Different surgical procedures have been proposed for the treatment of gingival recessions. The goal of this study was to compare the clinical results of gingival recession treatment using Subepithelial Connective Tissue Graft and an Acellular Dermal Matrix Allograft.
Materials and Methods:
The present study was performed on 5 patients with 9 bilateral Miller`s class I or II gingival recessions. This included 15 premolars and 3 canines. In each patient the teeth were randomly divided in two groups of test (ADMA) and control (SCTG). Clinical parameters including recession height (RH), recession width (RW), keratinized gingiva (KG), clinical attachment level (CAL) and probing depth (PD) were measured at baseline, 2, 4 and 6 months after surgery and data analysis was performed using the Wilcoxon signed rank test.Results:
The mean changes (mm) from baseline to 6 months in SCTG and ADMA were 2.22±0.83 and 1.77±0.66 decrease in RH, 2.55±0.88 and 2.33±0.86 decrease in RW, 1.44±0.88 and 2.0±1.11 increase in KG, 2.33±1.22 and 2.11±0.6 decrease in CAL and finally 0.22±0.66 and 0.33±0.7 decrease in PD, respectively. The differences in mean changes were not significant between the two groups in any of the parameters. The percentage of root coverage was 85.7% and 71.1% for the control and test group, respectively. The changes from baseline to the 6 month visit were significant for both groups in all parameters but PD.Conclusion:
Alloderm may be suggested as an acceptable substitute for connective tissue graft considering the root coverage effect and KG width increase. -
The aim of this case report was to present a case of multiple idiopathic apical root resorption which is a rare condition in a 17-year-old adult male. External root resorption of the permanent teeth is a multifactorial process. Well-recognized causes of apical root resorption in permanent teeth include orthodontic therapy, trauma, periapical or periodontal inflammation, tumors, cysts, occlusal stress, impacted teeth, systemic conditions, endocrine imbalances and dietary habits. When none of these causes are present, it is termed idiopathic root resorption which may be either cervical or apical. Multiple idiopathic apical root resorption is a rare condition which is usually detected as an incidental radiographic finding. However, it may cause pain and mobility in severe cases.