Comparison of various concentrations of tricalcium phosphate nanoparticles on mechanical properties and remineralization of fissure sealants.

Abstract

The aim of this study was to investigate the mechanical properties (flexural strength, micro-shear bond strength) and remineralizing potential of fissure sealants by adding various concentrations of β-tricalcium phosphate nanoparticles.This in-vitro study consisted of five experimental groups containing prepared nano-fisssure sealants (1-5 wt.% β-TCP nanoparticles) and two control groups containing a prepared and a commercial fissure sealant. Flexural/micro-shear bond strength values were measured using Zwick test machine. Cavities on sixty healthy premolar teeth were filled with the fissure sealants containing 0-5 wt.% of nano β-TCP. The samples were assessed for remineralization under scanning electron microscopy (SEM) and EDAX. Kolmogorov-Smirnov test, One-way ANOVA and Tukey's Post Hoc analysis/HSD were used to analyze the data.There was no significant difference between the flexural strengths/elastic modulus of the 0-5 wt.% nano β-TCP groups (p>0.05). The average flexural strength/elastic modulus of the prepared fissure sealant group (0%) was significantly higher than the commercial fissure sealant group (Clinpro) (p<0.05). There was no significant difference between micro-shear bond strengths of the experimental groups (1-5 wt.%), and between the commercial and the prepared (0%) fissure sealant groups (p>0.05). Examining the samples under SEM showed a significant increase in thickness of the intermediate layer with increasing concentrations of β-TCP nanoparticles (p<0.05).Addition of 1-5 wt.% β-TCP nanoparticles to the fissure sealants significantly increased the remineralization potential without affecting the mechanical properties.